Virgin Recycled Granules HDPE LDPE LLDPE Linear Low Density Polyethylene

Basic Info

Model NO.	types match-fit or recommended accordingly
Plastic Forming Method	Film/Extrusion/Blow/Injection
Color	White, Oyster White, Transparent, Customizable
Category	Plastic Raw Material, Virgin Granules, PE Granules
Shape/Form	Primary Granulated Form, Resins, Powder, Pellets
Export Market	America, Asia, Europe, Africa
Delivery Lead Time	15days
Shipping Terms	Fob, CNF, CFR, CIF, CPT, Negotiable
Payment	T/T, L/C, Negotiable
Price	Competitive, Costeffective, Low, Factory Price
Quality	Good, Prime
Certificate	Co, Coa, ISO
Inspection	SGS
After Sales Service	Good
Free Sample	Available
Inventory	Available
Code	Virgin, Recycled, Reprocessed
Application/Usage	Heavy Packaging Film, Shrink Film, Food Packaging
Transport Package	25kg/Bag, Customizable
Specification	granule of soybean size
Trademark	self produce, sinopec, customizable
Origin	China, China Mainland, Prc, People′s Republic of
HS Code	3901100001
Production Capacity	5000t/Year

Product Description

Product name:plastic raw material PE polyethylene virgin recycled granules pellets resins HDPE LLDPE LDPE
Color:White,transparent,customizable
TDS

Project		Test data	Data unit
Basic properties	Density	0.921	g/cm3
	Melt flow rate	0.3	g/10min
Mechanical properties	Elongation at break	≥450	%
	Tensile strength at break	≥13	Mpa

Performance			Test conditions [state]	Test method	Test data	Data unit
Basic properties	Density			ISO 1183	0.925	g/cm3
	Melt flow rate		2.16kg	ISO 1133	4	g/10min
Mechanical properties	Elongation	lengthways		ISO 527	550	%
		crosswise		ISO 527	700	%
	Tensile strength	lengthways		ISO 527	19	MPa
		crosswise		ISO 527	18	MPa
	Tensile strength			ISO 527	11	MPa
	Modulus of Elasticity			ISO 527	280	MPa
	Shore hardness			ISO 868	48
	Fall out of strength			ASTM D-1709	100	g
Thermal properties	Vicat softening point		A/50	ISO 306	94	ºC
	Melting point			ISO 11357	112	ºC

Project		Test data	Data unit
Basic properties	Density	0.9205~0.9245	g/cm3
	Melt flow rate	1.7-2.3	g/10min
Mechanical properties	Elongation at break	≥200	%
	Tensile strength at break	≥17	Mpa
	Tensile strength yield	≥3.0
	Shore hardness	≥44
Thermal properties	Vicat softening point	≥90	ºC

 

 

 

LLDPE 218WJ

Project	Test method	Test Data			Data Unit
MFR(190ºC,2.16ºC)		2			g/10min
Density		0.918			g/cm³
Yield tensile strength		MD	12		Mpa
		TD	10
Tensile strength at break		MD	35		MPa
		TD	29
Elongation at break		MD		700	%
		TD		750
Secant modulus		MD1%		220	Mpa
		TD1%		260
Haze		13			%
Elmandorf tear strength		MD		130	g
		TD		320
Vicat softening point		98			ºC
Glossiness		80